Annales de Chimie - Science des Matériaux

0151-9107
 

 ARTICLE VOL 31/2 - 2006  - pp.213-235  - doi:10.3166/acsm.31.213-235
TITRE
Étude cinétique de l'’oxydation à haute température et de la volatilisation de la chromine pour des superalliages de fonderie renforcés par carbures.
Partie I : Cas d’'alliages à base de nickel contenant du tantale

TITLE
A study of the kinetics of high temperature oxidation and chromia volatilization for carbides-strengthened cast superalloys.
Part I: The case of tantalum-containing nickel base alloys

RÉSUMÉ

Le comportement de trois alliages à base de nickel formeurs de chromine, de compositions Ni30Cr0,2C3Ta, Ni30Cr0,4C3Ta et Ni30Cr0,4C6Ta (%mass) en oxydation à 1 000, 1 100 et 1 200°C a été étudié. L'’analyse thermogravimétrique a été suivie de la détermination de la constante parabolique et de la constante de volatilisation de la chromine grâce à l'’analyse de l'’évolution de (Δm/S).[d(Δm/S)/dt] en fonction de -Δm/S, prise de masse par unité de surface, droite dont l’'ordonnée à l’'origine et la pente sont respectivement Kp et Kv. Les valeurs obtenues pour 1 200°C ont été validées par métallographie et comparaison de courbes. Carbone et tantale augmentent la constante parabolique tandis que le tantale diminue la constante de volatilisation.



ABSTRACT

The high temperature oxidation behaviour of three chromia-forming alloys, Ni30Cr0.2C3Ta, Ni30Cr0.4C3Ta and Ni30Cr0.4C6Ta (wt%), was studied by thermogravimetric measurements for 100 hours at 1000, 1100 and 1200°C. The data files were numerically treated in order to extract simultaneously the parabolic constant Kp and the linear volatilization constant Kv, which are the constant and the slope, respectively, of the straight line that represents (Δm/S).[d(Δm/S)/dt] versus-Δm/S (mass gain per unit surface area). The Kp and Kv values obtained for 1200°C were verified by performing microanalysis measurements and by controlling that the mathematical curves drawn with the assessed values of both Kp and Kv correctly fitted the experimental thermogravimetric curves. The comparison of all Kp and Kv values obtained for the three alloys at 1200°C allowed to see that high carbon and high tantalum contents obviously promote a higher rate of oxidation for the alloy. A higher carbon content also seems to lead to a quicker chromia volatilization, while tantalum tends, on the contrary, to reduce the volatilization of chromia.



AUTEUR(S)
Patrice BERTHOD, Lionel ARANDA, Céline VEBERT

Reçu le 30 mai 2005.    Accepté le 26 janvier 2006.

LANGUE DE L'ARTICLE
Français

 PRIX
• Abonné (hors accès direct) : 7.5 €
• Non abonné : 15.0 €
|
|
--> Tous les articles sont dans un format PDF protégé par tatouage 
   
ACCÉDER A L'ARTICLE COMPLET  (2,80 Mo)



Mot de passe oublié ?

ABONNEZ-VOUS !

CONTACTS
Comité de
rédaction
Conditions
générales de vente

 English version >> 
Lavoisier